Analisa Perbandingan Tegangan Pengelasan SMAW dan GTAW dengan Menggunakan Baja Ringan ST 37

Siswadi Siswadi, Navik Kholili, Royan Miftach, Alven Ritonga, Krisnadhi Hariyanto

Abstract


Abstract

Welding involves the process of heating and melting two parts of the object as well as the addition of additional material/electrodes to create a strong and durable connection. The method of welding, the type of material, the electrodes, and the model of the connection have an impact on the strength of the weld result. The purpose of the research is to determine the results of the traction strength of samples welded using the SMAW and GTAW welding methods, as well as to test the strength of the welding results and compare the strengths of welding SMAW, GTAW. The research method used for the test of traction is a universal test machine using the ASTM E8/E 8M-13a standard sample, a workpiece with a diameter of 0.6 cm, a length of 3 cm, fingers of 0,6 cm. The welding wire used is 0.26 cm and 0.2 cm in diameter, and a strong welding current of 90 ampere. GTAW welding was tested with pull and the result was a pull strength of 0.86 Kgf/mm2, a stretch strength of 19.24 Kgf/mm2, an extension rate of 100 percent with a strength of 2750 Kgf. The pull test on SMAW welding obtained the result of a pull force of 0,86 Kgf/mm2, the pull strength is 2.34 Kgf/mm2 and the length of extension reached 100 percent when tested at 2750 Kgf.

 

Keywords :

Traction, Welding Connections, Electric Welding, SMAW and GTAW Welding.

 

ABSTRAK

Pengelasan melibatkan proses pemanasan dan peleburan dua bagian benda serta penambahan bahan / elektroda tambahan untuk menciptakan sambungan yang kuat dan tahan lama. Metode pengelasan, jenis material, elektroda, dan model sambungan memiliki dampak terhadap kekuatan hasil las. Riset ini bertujuan untuk mengetahui hasil kekuatan tarik sampel yang dilas dengan metode pengelasan SMAW dan GTAW, disamping itu juga untuk menguji kekuatan hasil pengelasan dan membandingkan kekuatan las SMAW dan GTAW. Metode penelitian yang digunakan untuk pengujian tarik adalah mesin uji universal dengan menggunakan sampel standar ASTM E8/E 8M-13a, benda kerja dengan diameter 0,6 cm, panjang 3 cm, jari-jari 0,6 cm. Kawat las yang digunakan berdiameter 0,26 cm dan 0,2 cm, serta kuat arus pengelasan 90 ampere. Pengelasan GTAW di uji tarik dan hasil yang diperoleh adalah kekuatan tarik 0,86 Kgf/mm2, kekuatan regangan 19,24 Kgf/mm2, tingkat pemanjangan mencapai 100 persen dengan kekuatan 2750 Kgf. Pengujian tarik pada pengelasan SMAW didapatkan hasil kekuatan tarik 0,86 Kgf/mm2, kekuatan regangan adalah 2,34 Kgf/mm2 dan tingkat pemanjangan mencapai 100 persen saat diuji tarik dengan kekuatan 2750 Kgf. Kesimpulan yang didapatkan dari pengujian ini adalah jenis sambungan yang digunakan dalam proses pengelasan memiliki kekuatan tarik 0,86 Kgf/mm2 dengan nilai tertinggi mencapai 53,43 Kgf/mm2 pada metode SMAW dan kekuatan tarik terendah 32,32 Kgf/mm2 dengan beban seberat 2750 Kgf.

 

Kata Kunci :

Kekuatan tarik, Sambungan las, Las listrik, Pengelasan SMAW dan GTAW

Keywords


Kekuatan Tarik; Sambungan Las; Las Listrik; Pengelasan SMAW dan GTAW

Full Text:

PDF

References


Alaeibehmand, S., Mirsalehi, S. E., & Ranjbarnodeh, E. (2021). Pinless FSSW of DP600/Zn/AA6061 dissimilar joints. Journal of Materials Research and Technology, 15, 996–1006. https://doi.org/10.1016/j.jmrt.2021.08.071

Ali, M. M., & Kh, M. M. (2020). Effects Of Welding Parameters On Characterization And Mechanical Properties Of Steel 37 Weldments (Vol. 48, Issue 2).

Arizal, H., Ramadani, A. H., & Abdi, F. I. (2020). Pengaruh Tekanan Bahan Bakar Terhadap Emisi Gas Buang Pada Mesin K3-Ve. Otopro, 16(1), 23. https://doi.org/10.26740/otopro.v16n1.p23-28

Azwinur, Syukran, Akhyar, & Ferdiyansyah. (2022). The Effect of Electrode Type on The Tensile Strength Characteristics of Welded Joints Between SA.240 Tp.304 Stainless Steel and SA.36 Carbon Steel Alloys through SMAW Welding Process. International Journal of Integrated Engineering, 14(4), 35–42. https://doi.org/10.30880/ijie.2022.14.04.004

Bawazir, M. Z., Sariyusda, & Darmein. (2022). Analisa Hasil Pengelasan Smaw Pada Sistem Sambungan Pipa Aisi C-1020 Steam H2O2 (Boiler) Secara Dt Dan Ndt Pada PT. Pupuk Iskandar Muda. Jurnal Mesin Sains Terapan, 6(2), 104–109.

Fikrie, A., Dwi Pratiwi, W., & Fakhri, A. A. (2022). Overlay Welding Analysis On GTAW And SMAW Processes In Terms Of Mechanical Properties And Corrosion Rate. Journal of Engineering and Applied Technology Online, 3(2), 87–93. https://journal.uny.ac.id/index.php/jeatech

Gusniar, I. N., Juhri, A., & Noubnome, V. (2021). Pengaruh Variasiarus Dan Posisi Pengelasan SMAW Terhadap Sifat Mekanik Baja ST 37. Jurnal Teknik Mesin, 14(2), 134–139. https://doi.org/10.30630/jtm.14.2.591

Harahap, J., Wahyudin, Hasnita, & Lutfhi. (2022). Analisis Eksperimental Dan Numerik Uji Tarik Hasil Pengelasan Smaw Pada Baja Karbon Rendah Dengan Variasi Jenis Elektroda Terhadap Sifat Mekanis. Vocational Education and Technology Journal, 4(September), 8–17.

Irwan, M. (2020). Analisis Kekuatan Tarik Baja ST42 Dengan Variasi Pendinginan Pasca Pengelasan. 1, 7–12.

Iswanto, P. T., Mudjijana, & Himarosa, R. A. (2017). Karakterisasi Sambungan SMAW Baja Karbon Rendah Menggunakan 3 Jenis Elektroda. Material Dan Proses Manufaktur, 1(2), 103–109.

Jorge, L. D. J., Cândido, V. S., Silva, A. C. R. Da, Garcia Filho, F. D. C., Pereira, A. C., Luz, F. S. Da, & Monteiro, S. N. (2018). Mechanical properties and microstructure of SMAW welded and thermically treated HSLA-80 steel. Journal of Materials Research and Technology, 7(4), 598–605. https://doi.org/10.1016/J.JMRT.2018.08.007

Karmawan, W., Adja, H. B., Alvindo, N. V, Handoko, K. T., Pradana, J., Zakkaria, L. N., Zuhron, M., Jaya, H. T. S., & Subardi, A. (2020). Analisa Kekuatan Variasi Arus Las SMAW Dengan Elektroda E 7018 Bahan Baja ST 42 Terhadap Sifat Mekanis. Oktober 2020 Jurnal JMMME, 1(2), 19.

Ostovan, F., Shafiei, E., Toozandehjani, M., Mohamed, I. F., & Soltani, M. (2021). On the role of molybdenum on the microstructural, mechanical and corrosion properties of the GTAW AISI 316 stainless steel welds. Journal of Materials Research and Technology, 13, 2115–2125. https://doi.org/10.1016/j.jmrt.2021.05.095

Rangaswamy, H., M, H. H., Gowdru Chandrashekarappa, M. P., Pimenov, D. Y., Giasin, K., & Wojciechowski, S. (2021). Experimental investigation and optimization of compression moulding parameters for MWCNT/glass/kevlar/epoxy composites on mechanical and tribological properties. Journal of Materials Research and Technology, 15, 327–341. https://doi.org/10.1016/j.jmrt.2021.08.037

Ridzkiansyah, R. D. M., & Irwan, Y. (2021). Analisa Pengaruh Jenis Elektroda Pengelasan SMAW Pada Penyambungan Baja ASTM A36 Dengan Baja Tahan Karat AISI 304 Terhadap Sifat Mekanis. Desiminasi FTI, 1–6.

Saputra, H., Ivanto, M., & Lubis, G. S. (2023). Pengaruh Hasil Pengelasan Model Smaw Terhadap Kekuatan Tarik Baja ST 37 Dan ASTM A36. 4(1), 55–64.

Saputra, R., & Widjayanto, A. (2019). Analisis Perbandingan Kekuatan Tarik Connecting Rod Asli Dengan Imitasi Pada Sepeda Motor. Bina Teknika, 15(1), 13. https://doi.org/10.54378/bt.v15i1.885

Saxena, A., Kumaraswamy, A., Madhusudhan Reddy, G., & Madhu, V. (2018). Influence of welding consumables on tensile and impact properties of multi-pass SMAW Armox 500T steel joints vis-a-vis base metal. Defence Technology, 14(3), 188–195. https://doi.org/10.1016/j.dt.2018.01.005

Vaikar, S. J., Narayanan, V., George, J. C., Kanish, T. C., & Ramkumar, K. D. (2022). Effect of weld microstructure on the tensile properties and impact toughness of the naval, marine-grade steel weld joints. Journal of Materials Research and Technology, 19, 3724–3737. https://doi.org/10.1016/j.jmrt.2022.06.104

Wijoyo, W., Mujahid, M., Nurhidayat, A., Surjadi, E., & Saefuloh, I. (2021). The effect of current strength on tensile strength and impact toughness of cast iron welded joints. Teknika: Jurnal Sains Dan Teknologi, 17(2), 125. https://doi.org/10.36055/tjst.v17i2.11216

Winardi, Y., Fadelan, F., Munaji, M., & Krisdiantoro, W. N. (2020). Pengaruh Elektroda Pengelasan Pada Baja AISI 1045 Dan SS 202 Terhadap Struktur Mikro Dan Kekuatan Tarik. Jurnal Pendidikan Teknik Mesin Undiksha, 8(2), 86. https://doi.org/10.23887/jptm.v8i2.27772




DOI: https://doi.org/10.38038/vocatech.v5i2.172

Refbacks

  • There are currently no refbacks.


VOCATECH : Vocational and Technology Journal
Unit Penelitian dan Pengabdian Masyarakat & Penjaminan Mutu
Akademi Komunitas Negeri Aceh Barat
Komplek STTU Alue Peunyareng, Ujong Tanoh Darat, Meureubo, Kabupaten Aceh Barat, Aceh 23615
Telp. (0655) 7110271
Email: vocatech@aknacehbarat.ac.id

VOCATECH: Vocational Education and Technology Journal Published by:
Unit Penelitian dan Pengabdian Masyarakat & Penjaminan Mutu
Akademi Komunitas Negeri Aceh Barat

Indexed by:

GS2 logoCrossref logoGaruda logosinta-5 logosinta-5 logo
Creative Commons License logo

VOCATECH: Vocational Education and Technology Journal Creative Commons Attribution-ShareAlike 4.0 International License.